Journal of Shandong University(Engineering Science) ›› 2023, Vol. 53 ›› Issue (1): 1-10.doi: 10.6040/j.issn.1672-3961.0.2022.137

• Transportation Engineering-special topics on road materials •     Next Articles

Comprehensive properties of red mud asphalt mixture based on organic and inorganic modification

Jizhe ZHANG1(),Zixuan GANG1,Yufeng BI2,Hongya YUE2,Run XU2,Tingting DING2,Shijie QI2   

  1. 1. School of Qilu Transportation, Shandong University, Jinan 250002, Shandong, China
    2. Shandong Provincial Communications Planning and Design Institute Co., Ltd., Jinan 250101, Shandong, China
  • Received:2022-04-06 Online:2023-02-20 Published:2023-02-13

Abstract:

Focused on the issues of red mud utilization and road building material shortage, this paper put forward the research idea of utilizing red mud as the succedaneum of limestone powder to prepare asphalt mixture. Modification methods which included inorganic powder blending (cement, slaked lime) and organic coupling agent surface modification (silane coupling agent KH-550, KH-560) were proposed with the view of solving moisture sensitivity of red mud-bitumen interface, with the influence of modification means on performance of red mud asphalt mixture were also studied. The performance of red mud asphalt mixture before and after modification were systematically evaluated by using dynamic stability test, Marshall test, Hamburg rut test, dynamic modulus test and two-point bending fatigue test. It was found that the red mud could improve the high-temperature performance of asphalt mixture, but had negative effects on the moisture stability, cracking resistance and fatigue life. After red mud modification, the high and low temperature performance, moisture stability and long-term durability of red mud asphalt mixture were improved to varying degrees, and the surface modification effect of silane coupling agent performed better. It was proved the feasibility of using red mud to produce asphalt mixture and provided a new approach for red mud utilization.

Key words: red mud, asphalt mixture, modification, moisture stability, fatigue

CLC Number: 

  • U414

Table 1

Basic performance indicators of 70# matrix bitumen"

指标 软化点/℃ 针入度(25 ℃)/(0.1 mm) 延度(15 ℃)/cm
结果 46.2 68.3 >150
规范要求 ≥46.0 60.0~80.0 ≥100

Table 2

Specific surface area of different powder materials"

粉体种类 比表面积/(m2·g-1)
矿粉 0.502
赤泥 22.265
消石灰 9.693
水泥 1.538

Table 3

Gradation composition of AC-20 asphalt mixture"

矿料组成 筛孔尺寸/mm 级配组成/%
集料 15~20 24
10~15 20
5~10 21
3~5 11
0~3 19
矿粉 5

Table 4

Density of different powders"

填料 密度/(g·cm-3)
矿粉 2.775
赤泥 2.613
消石灰 2.319
水泥 3.210
KH-550改性赤泥 2.587
KH-560改性赤泥 2.598

Table 5

Filler composition and sample ID of asphalt mixtures"

样品编号 填料组成
AC-LP 石灰岩矿粉
AC-RM 赤泥
AC-RH m(赤泥)∶m(消石灰)=9∶1
AC-RP m(赤泥)∶m(水泥)=9∶1
AC-R550 m(赤泥)∶m(硅烷偶联剂550)=100∶1
AC-R560 m(赤泥)∶m(硅烷偶联剂560)=100∶1

Table 6

Dynamic stability of asphalt mixtures"

混合料类型 动稳定度/(次·mm-1)
AC-LP 880
AC-RM 1086
AC-RH 1255
AC-RP 1194
AC-R550 1270
AC-R560 1250

Table 7

Maximum bending strain of asphalt mixture"

混合料类型 弯拉应变/10-3
AC-LP 4.106
AC-RM 3.869
AC-RH 4.583
AC-RP 4.438
AC-R550 4.649
AC-R560 4.598

Table 8

Marshall residual stability of asphalt mixtures"

混合料类型 残留稳定度/%
AC-LP 87.8
AC-RM 67.1
AC-RH 86.3
AC-RP 84.9
AC-R550 91.8
AC-R560 86.7

Fig.1

Hamburg rutting of asphalt mixtures under 50 ℃ dry condition"

Fig.2

Hamburg rutting of asphalt mixtures under 50 ℃ water bath condition"

Fig.3

Dynamic modulus of asphalt mixtures at different temperatures"

Fig.4

Phase angle of asphalt mixtures at different temperatures"

Table 9

Dynamic modulus and phase angle at different temperatures at 10 Hz"

混合料类型 5 ℃ 20 ℃ 35 ℃ 50 ℃
动态模量/ MPa 相位角/ (°) 动态模量/ MPa 相位角/ (°) 动态模量/ MPa 相位角/ (°) 动态模量/ MPa 相位角/ (°)
AC-LP 20 496 11.62 8722 25.83 3097 36.63 708.6 38.32
AC-RM 17 637 10.48 9700 25.67 3007 36.03 724.0 36.24
AC-RH 20 644 10.09 10 160 25.47 3149 35.90 732.5 35.89
AC-RP 21 910 9.66 10 842 23.97 3353 36.87 787.5 37.77
AC-R550 21 918 11.78 10 470 25.91 3216 36.89 798.0 38.41
AC-R560 20 674 12.01 10 130 25.99 3197 36.97 793.0 38.19

Table 10

Fatigue life of different asphalt mixtures"

混合料类型 疲劳寿命/次
AC-LP 104 147
AC-RM 45 746
AC-RH 61 548
AC-RP 70 948
AC-R550 94 361
AC-R560 86 732
1 张兰芳. 碱激发矿渣水泥和混凝土[M]. 成都: 西南交通大学出版社, 2018: 36- 37.
ZHANG Lanfang . Alkali activated slag cement and concrete[M]. Chengdu: Southwest Jiaotong University Press, 2018: 36- 37.
2 许智芳, 苏爱琴, 张新峰. 氧化铝赤泥的综合回收及利用现状[J]. 山东冶金, 2010, 32 (3): 8- 12.
doi: 10.16727/j.cnki.issn1004-4620.2010.03.027
XU Zhifang , SU Aiqin , ZHANG Xinfeng . Compre-hensive recovery and utilization status of alumina red mud[J]. Shandong Metallurgy, 2010, 32 (3): 8- 12.
doi: 10.16727/j.cnki.issn1004-4620.2010.03.027
3 李卓智. 道路工程应用拜耳法赤泥的路用性能与强度机理研究[D]. 济南: 山东大学, 2018.
LI Zhuozhi. Research on pavement properties and solidification mechanism of engineering stabilized Bayer red mud[D]. Jinan: Shandong University, 2018.
4 赵广慧. 铝工业固体废物: 赤泥综合治理[J]. 科技信息, 2011, (5): 373- 390.
ZHAO Guanghui . Solid waste from aluminum industry: comprehensive treatment of red mud[J]. Science and Technology Information, 2011, (5): 373- 390.
5 南相莉, 张廷安, 刘燕. 我国赤泥综合利用分析[J]. 过程工程学报, 2010, 10, 264- 270.
NAN Xiangli , ZHANG Tingan , LIU Yan . Analysis of comprehensive utilization of red mud in China[J]. The Chinese Journal of Process Engineering, 2010, 10, 264- 270.
6 叶楠. 拜耳法赤泥活化预处理制备地聚合物及形成强度机理研究[D]. 武汉: 华中科技大学, 2016.
YE Nan. Study on the preparation of geopolymer from pretreated Bayerred mud and mechanism of the strength formation[D]. Wuhan: Huazhong University of Science and Technology, 2016.
7 YAO L Y , GAO W Y , MA X Y , et al. Properties analysis of asphalt binders containing Bayer red mud[J]. Materials, 2020, 13 (5): 1122.
doi: 10.3390/ma13051122
8 FU T, BAO H M, DUAN X X. Molecular simulation study on modification mechanism of red mud modified asphalt[C]//IOP Conference Series: Earth and Environmental Science. Singapore: IOP Publishing, 2017, 100(1): 012005.
9 FU T , WEI J H , BAO H M , et al. Multiscale study on the modification mechanism of red mud modified asphalt[J]. Advances in Materials Science and Engineering, 2020, 2150215.
10 ZHANG H J , LI H , ZHANG Y , et al. Performance enhancement of porous asphalt pavement using red mud as alternative filler[J]. Construction and Building Materials, 2018, 160, 707- 713.
doi: 10.1016/j.conbuildmat.2017.11.105
11 ZHANG H J , LI H , ABDELHADY A , et al. Optimum filler-bitumen ratio of asphalt mortar considering self-healing property[J]. Journal of Materials in Civil Engineering, 2019, 31 (8): 04019166.
doi: 10.1061/(ASCE)MT.1943-5533.0002792
12 ZHANG H J , LI H , ABDELHADY A , et al. Utilization of fine solid waste in asphalt mortar[J]. Journal of Testing and Evaluation, 2019, 47 (6): 4523- 4534.
13 包惠明, 吕总威, 张亦敏. 赤泥改性沥青黏温特性分析[J]. 筑路机械与施工机械化, 2019, 36 (8): 64- 68.
BAO Huiming , LÜ Zongwei , ZHANG Yimin . Analysis of viscosity-temperature properties of red mud modified asphalt[J]. Road Construction Machinery and Construction Mechanization, 2019, 36 (8): 64- 68.
14 包惠明, 傅涛. 赤泥的综合利用现状分析[J]. 矿产综合利用, 2018, (5): 6- 12.
BAO Huiming , FU Tao . Analysis of comprehensive utilization of red mud[J]. Comprehensive Utilization of Minerals, 2018, (5): 6- 12.
15 包惠明, 牟卡莉. 赤泥改性沥青相容性研究[J]. 公路, 2018, 63 (3): 208- 211.
BAO Huiming , MU Kali . Study on compatibility of red mud modified asphalt[J]. Highway, 2018, 63 (3): 208- 211.
16 包惠明, 牟卡莉. 赤泥改性沥青黏度及微观特性[J]. 河南科技大学学报(自然科学版), 2017, 38 (5): 47- 50.
BAO Huiming , MU Kali . Viscosity and microscopic characteristics of red mud modified asphalt[J]. Journal of Henan University of Science and Technology(Natural Science Edition), 2017, 38 (5): 47- 50.
17 LIMA M S S , THIVES L P . Evaluation of red mud as filler in Brazilian dense graded asphalt mixtures[J]. Construction and Building Materials, 2020, 260, 119894.
18 ZHANG J Z , LIU S J , YAO Z Y , et al. Environmental aspects and pavement properties of red mud waste as the replacement of mineral filler in asphalt mixture[J]. Construction and Building Materials, 2018, 180, 605- 613.
19 ZHANG J Z , SUN C J , LI P Z , et al. Experimental study on rheological properties and moisture suscep-tibility of asphalt mastic containing red mud waste as a filler substitute[J]. Construction and Building Materials, 2019, 211, 159- 166.
20 ZHANG J Z , LI P Z , LIANG M , et al. Utilization of red mud as an alternative mineral filler in asphalt mastics to replace natural limestone powder[J]. Construction and Building Materials, 2020, 237, 117821.
21 王民, 朱梦良, 王英俊, 等. 水泥代替矿粉对沥青混合料性能的影响分析[J]. 重庆建筑大学学报, 2007, 29 (6): 121- 125.
WANG Min , ZHU Mengliang , WANG Yingjun , et al. Effect of substitution of mineral powder by cement on asphalt mixture performance[J]. Journal of Chongqing Jianzhu University, 2007, 29 (6): 121- 125.
22 高及阳, 曾梦澜, 孙志林. 改性纳米SiO2对再生沥青胶结料性能的影响[J]. 土木工程学报, 2019, 52 (3): 120- 128.
GAO Jiyang , ZENG Menglan , SUN Zhilin . Effects of nano-SiO2 with modified surface on properties of recycled asphalt binder[J]. Journal of Civil Engineering, 2019, 52 (3): 120- 128.
23 张宝龙, 吴平, 闫新勇, 等. 表面修饰粉煤灰对沥青路用性能的影响[J]. 长安大学学报(自然科学版), 2018, 38 (3): 43- 51.
ZHANG Baolong , WU Ping , YAN Xinyong , et al. Effect of surface-modified fly ash on engineering performance of asphalt[J]. Journal of Chang'an University (Natural Science Edition), 2018, 38 (3): 43- 51.
24 董仕豪, 韩森, 尹媛媛, 等. 基于表面能理论的石灰改性沥青黏附性研究[J]. 重庆交通大学学报(自然科学版), 2021, 40 (3): 89- 97.
DONG Shihao , HAN Sen , YIN Yuanyuan , et al. Adhesion of lime modified asphalt based on surface energy theory[J]. Journal of Chongqing Jiaotong University (Natural Science Edition), 2021, 40 (3): 89- 97.
25 周志刚. 硅烷偶联剂的水解工艺研究[J]. 石化技术, 2022, 29 (4): 220- 221.
ZHOU Zhigang . Hydrolysis process of silane coupling agent[J]. Petrochemical Technology, 2022, 29 (4): 220- 221.
26 中华人民共和国交通运输部. 公路工程集料试验规程: JTG E42-2005[S]. 北京: 人民交通出版社, 2005.
Traffic transportation department of the people's republic of China. Test Methods of Aggregate for Highway Engineering: JTG E42-2005[S]. Beijing: China Communication Press, 2005.
27 中华人民共和国交通运输部. 公路沥青路面施工技术规范: JTG F40-2004[S]. 北京: 人民交通出版社, 2004.
Traffic transportation department of the people's republic of China. Technical Specifications for Construction of Highway Asphalt Pavements: JTG F40-2004[S]. Beijing: China Communication Press, 2004.
28 中华人民共和国交通运输部. 公路工程沥青及沥青混合料试验规程: JTG E20-2011[S]. 北京: 人民交通出版社, 2011.
Traffic transportation department of the people's republic of China. JTG E20-2011, Standard test methods of bitumen and bituminous mixtures for highway engineering[S]. Beijing: China Communication Press, 2011.
29 AASHTO. Standard method of test for Hamburg wheel-track testing of compacted hot mix asphalt (HMA): T 324-14[S]. Washington DC: American Association of State Highway and Transportation Officials, 2014.
30 CHEN T , LUAN Y C , MA T , et al. Mechanical and microstructural characteristics of different interfaces in cold recycled mixture containing cement and asphalt emulsion[J]. Journal of Cleaner Production, 2020, 258, 120674.
31 ZHANG H J , LI H , ABDEL-HADY A , et al. Optimum filler-bitumen ratio of asphalt mortar considering self-healing property[J]. Journal of Materials in Civil Engineering, 2019, 31 (8): 04019166.
32 中华人民共和国交通运输部. 公路沥青路面设计规范: JTG D50-2017[S]. 北京: 人民交通出版社, 2017.
Traffic transportation department of the people's republic of China. Specifications for Design of Highway Asphalt Pavement: JTG D50-2017[S]. Beijing: China Communication Press, 2017.
[1] WANG Zhongxiao, CUI Xinzhuang, CUI Sheqiang, ZHANG Lei, CHE Huaqiao, SU Junwei. The influence of soil-cement pile deterioration and modification in salt-water area on road composite foundation [J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2018, 48(4): 69-77.
[2] GUO Dedong, ZHANG Shengtao, LI Jin, ZHANG Long, ZHANG Xibin. Migration behavior of reclaimed mineral aggregate in process of central plant hot recycling [J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2018, 48(2): 46-52.
[3] LIU Lijun, ZHANG Hongxing, ZHANG Weijie, WANG Gang, QI Meng. The property of die-casting dies of wiper repaired by laser welding with filler wire [J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2015, 45(3): 73-79.
[4] LIU Chang-tian1, LI Qing-liang2, LI Ying-jie1*, SUN Rong-yue1, LU Chun-mei1. Cyclic carbonation characteristics of limestone modified by waste wood vinegar [J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2013, 43(3): 82-86.
[5] ZHU Deng-yuan1, 2, YAO Zhan-yong1*, GUAN Yan-hua1, ZHUANG Pei-zhi1. Balance analysis of the pavement structure based on failure approach index [J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2012, 42(6): 74-79.
[6] GUO Yin-tao1, 2, LIU Qing-quan2, LIU Zhen-qing3, WANG Song-gen3. Properties of semi-flexible cold recycled asphalt mixtures using modified emulsified asphalt and cement binders [J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2012, 42(3): 81-86.
[7] LI Xiao-juan, HAN Sen, JIA Zhi-qing, ZHANG Li-juan. Research of  the crack resistance of asphalt mixture based on the low-temperature bending test [J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2010, 40(6): 88-93.
[8] BA Huan-fen, SHI Lai-shun*, LIU Yan-pu. The solvent effect on  polyethylene terephthalate surface modification by plasma induced grafting polymerization of acrylic acid [J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2010, 40(6): 107-112.
[9] LI Hua-luan1, GAO Pei-fa2, MU Nai-min3, WANG Lin2. Experiments on dispersive soil identification and modification [J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2010, 40(4): 92-95.
[10] LIU Yan-Pu, Shi-Lai-Shun, Ba-Huan-Fen, Guo-Fang. The investigation of polyethylene surface modification by cold plasma induced grafting polymerization of acrylonitrile [J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2009, 39(5): 124-127.
[11] YANG Yongshun1, WANG Lin2, GAO Xuechi1, JIA Haiqing3, WEI Jincheng2. Analysis of perpetual pavement strain distribution and fatigue damage [J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2009, 39(2): 118-124.
[12] LI Cheng-feng. Study  of surface modification of hydroxyapatite powers by ions of ferrous iron [J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2008, 38(6): 87-90.
[13] YANG Yong-shun,CAO Wei-dong,LI Ying-yong,ZHANG Chong-gao . Preparation process and performance of asphalt-rubber [J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2008, 38(5): 10-13 .
[14] YAO Zhan-yong,WU Shi-mei,CHEN Chao . Variance research on pavement fatigue failure caused by the crown [J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2007, 37(6): 87-90 .
[15] LIU Shu-tang,ZHANG Hao,FENG Yong . Research on the relationship of the optimum asphalt ratios between similar [J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2006, 36(6): 91-94 .
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
[1] WANG Su-yu,<\sup>,AI Xing<\sup>,ZHAO Jun<\sup>,LI Zuo-li<\sup>,LIU Zeng-wen<\sup> . Milling force prediction model for highspeed end milling 3Cr2Mo steel[J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2006, 36(1): 1 -5 .
[2] ZHANG Yong-hua,WANG An-ling,LIU Fu-ping . The reflected phase angle of low frequent inhomogeneous[J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2006, 36(2): 22 -25 .
[3] LI Kan . Empolder and implement of the embedded weld control system[J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2008, 38(4): 37 -41 .
[4] SHI Lai-shun,WAN Zhong-yi . Synthesis and performance evaluation of a novel betaine-type asphalt emulsifier[J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2008, 38(4): 112 -115 .
[5] KONG Xiang-zhen,LIU Yan-jun,WANG Yong,ZHAO Xiu-hua . Compensation and simulation for the deadband of the pneumatic proportional valve[J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2006, 36(1): 99 -102 .
[6] LAI Xiang . The global domain of attraction for a kind of MKdV equations[J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2006, 36(1): 87 -92 .
[7] YU Jia yuan1, TIAN Jin ting1, ZHU Qiang zhong2. Computational intelligence and its application in psychology[J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2009, 39(1): 1 -5 .
[8] LI Liang, LUO Qiming, CHEN Enhong. Graph-based ranking model for object-level search
[J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2009, 39(1): 15 -21 .
[9] CHEN Rui, LI Hongwei, TIAN Jing. The relationship between the number of magnetic poles and the bearing capacity of radial magnetic bearing[J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2018, 48(2): 81 -85 .
[10] WANG Bo,WANG Ning-sheng . Automatic generation and combinatory optimization of disassembly sequence for mechanical-electric assembly[J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2006, 36(2): 52 -57 .