酸蚀时间对喷砂后TC4钛合金表面形貌及抗腐蚀性的影响

doi:10.6040/j.issn.1672-3961.0.2017.003

Abstract

Abstract: TC4 Titanium plates were etched by HCl/H₂SO₄ mixture after being blasted by Al₂O₃ particles of size 220 to investigate the effect of different etching time(0.5,1, 2 and 3 h)on the surface morphology and corrosion resistance, while the polishing treatment was set as the control group. The surface morphology of the titanium alloy samples was characterized by scanning electron microscopy(SEM)and 3D laser confocal microscopy followed by the surface roughness measurement. Then the corrosion resistance measurement was carried out by the electrochemical workstation to evaluate the corrosion behavior of all samples. The results showed that with the prolongation of etching time, the surface morphology of titanium alloy tended to be homogenized from clutter, and the roughness first rose and then decreased. Group 2 h had the maximum roughness and the highest proportion of surface micropores, and the interface expansion area ratio was 222%. In terms of corrosion resistance, all of the sandblasting and acid-etching(SLA)groups performed better than the polishing group, indicating that the SLA treatment can be beneficial for generating oxide film which possesses better corrosion resistance. Besides, with the extending of etching time, the corrosion tendency was smaller, and the group 3 h performed the best of all groups.

Key words: titanium, implant, microporous structure, sandblasting and acid-etching, corrosion resistance

CLC Number:

TG162.2

REN Bing, WAN Yi, WANG Guisen, WANG Teng. Influence of different acid-etching time on the surface morphology and corrosion resistance of TC4 titanium alloys after sandblasting[J].JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2017, 47(3): 139-142.

References

[1] ZHANG D C, WANG Y, LIN J G, et al. Microstructure and superelasticity of a biomedical β-type titanium alloy under various processing routes[J]. Applied Materials Today, 2016, 5: 41-51.
[2] ASSIS S LD, WOLYNEC S, COSTA I. Corrosion characterization of titanium alloys by electrochemical techniques[J]. Electrochimica Acta, 2006, 51(8-9): 1815-1819.
[3] PINA V G, AMIGÓ V, MU(~overN)OZ A I. Microstructural, electrochemical and tribo-electrochemical characterisation of titanium-copper biomedical alloys[J]. Corrosion Science, 2016, 109: 115-125.
[4] LIANGS X, FENG X J, YIN L X, et al. Development of a new β Ti alloy with low modulus and favorable plasticity for implant material[J]. Materials Science and Engineering: C, 2016, 61: 338-343.
[5] 于振涛, 韩建业, 麻西群, 等. 生物医用钛合金材料的生物及力学相容性[J]. 中国组织工程研究, 2013, 17(25): 4707-4714. YU Zhentao, HAN Jianye, MAXiqun, et al. Biological and mechanical compatibility of biomedical titanium alloy materials[J]. Chinese Journal of Tissue Engineering Research, 2013, 2(4):175-202.
[6] 赵凤娟, 宋英, 王福平. 医用钛合金及其表面活化的研究现状[J]. 金属热处理, 2009, 34(2): 106-110. ZHAO Fengjuan, SONG Ying, WANG Fuping. Research status of biomedical titanium alloy and its surface activation[J]. Heat Treatment of Metals, 2009, 34(2):106-110.
[7] WEI D, FENG W, DU Q, et al. Titania nanotube/nano-brushite composited bioactive coating with micro/nanotopography on titanium formed by anodic oxidation and hydrothermal treatment[J]. Ceramics International, 2015, 41(10): 13115-13125.
[8] 马凯, 赵宝红, 邓春富. 医用钛及钛合金牙种植体生物相容性及其相关抗菌性能研究进展[J]. 中国实用口腔科杂志, 2016, 9(7): 441-445. MA Kai, ZHAO Baohong, DENG Chunfu. Research advances on the biocompatibility and related antibacterial properties of biomedical titanium and titanium alloy dental implants[J]. Chinese Journal of Practical Stomatology, 2016, 9(7):441-445.
[9] 王桂森, 万熠, 王滕, 等. 植入体微纳结构表面制备及生物相容性研究综述[J]. 表面技术, 2016, 45(5): 8-18. WANG Guisen, WAN Yi, WANG Teng, et al. Review on preparation of micro-nano structure on implant surface and its biocompatibility[J]. Surface Technology, 2016, 45(5): 8-18.
[10] 焦岩. 生物医用钛合金表面处理及其微结构[D]. 大连: 大连理工大学, 2013. JIAO Yan. Surface treatment and microstructure of biomedical titanium alloy[D]. Dalian: Dalian University of Technology, 2013.
[11] GROTBERG J, HAMLEKHAN A, BUTT A, et al. Thermally oxidized titania nanotubes enhance the corrosion resistance of Ti6Al4V[J]. Materials Science and Engineering: C, 2016, 59: 677-689.
[12] ZAVERI N, MCEWEN G D, KARPAGAVALLI R, et al. Biocorrosion studies of TiO2 nanoparticle-coated Ti—6Al—4V implant in simulated biofluids[J]. Journal of Nanoparticle Research, 2010, 12(5): 1609-1623.
[13] 王明, 宋西平. 医用钛合金腐蚀、力学相容性和生物相容性研究现状[J]. 钛工业进展, 2008, 25(2): 13-18. WANG Ming, SONG Xiping. Study actuality of corrosion, mechanical compatibility and biocompatibility of titanium alloys for medical application[J]. Titanium Industry Progress, 2008, 25(2):13-18.
[14] 杨东, 郭金明. 钛合金的腐蚀机理及耐蚀钛合金的发展现状[J]. 钛工业进展, 2011, 28(2): 4-7. YANG Dong, GUO Jinming. Corrosion mechanism of titanium alloys and development of corrosion-resistance titanium alloys[J]. Titanium Industry Progress, 2011, 28(2): 4-7.
[15] CAI Z, NAKAJIMA H, WOLDU M, et al. In vitro corrosion resistance of titanium made using different fabrication methods[J]. Biomaterials, 1999, 20(2):183-190.
[16] CHANDER K P, VASHISTA M, SABIRUDDIN K, et al. Effects of grit blasting on surface properties of steel substrates[J]. Materials & Design, 2009, 30(8): 2895-2902.
[17] SEN D, CHAVAN N M, RAO D S, et al. Influence of grit blasting on the roughness and the bond strength of detonation sprayed coating[J]. Journal of Thermal Spray Technology, 2010, 19(4): 805-815.
[18] 张松营. 医用钛合金表面不同粒度Al₂O₃喷砂酸蚀及多巴胺涂层研究[D]. 兰州:兰州大学, 2014. ZHANG Songying. Surface treatments of medical titanium alloy by Al₂O₃ blasting with different sizes and acid etching and dopamine coating[D]. Lanzhou: Lanzhou University, 2014.
[19] 王亚敏. 不同粗化喷砂-酸蚀纯钛表面的性能研究[D]. 广州:南方医科大学, 2011. WANG Yamin. The investigation of different roughed sandblasted/alumina/acid etched titanium surfaces[D]. Guangzhou: Southern Medical University, 2011.
[20] 董菲, 丁仲鹃, 牛涛. TiO₂喷砂酸蚀处理对钛片表面氧化膜及成骨细胞生长影响的研究[J]. 华西口腔医学杂志, 2008, 26(1): 10-14. DONG Fei, DING Zhongjuan, NIU Tao. Effects of TiO₂ blasted and acid-etched titanium surfaces on oxide-film and osteoblast[J]. West China Journal of Stomatology, 2008, 26(1):10-14.
[21] 董福生, 栗兴超, 孙士军. 纯钛种植体粗化表面的构建及形貌分析[J]. 中国口腔种植学杂志, 2009(2):6-7. DONG Fusheng, LI Xingchao, SUN Shijun. Construction of roughness treatment to pure titanium implant surface and topography analysis[J]. Chinese Journal of Oral Implantology, 2009(2): 6-7.
[22] LIN Z, WANG Y, WANG D, et al. Porous structure preparation and wettability control on titanium implant[J]. Surface and Coatings Technology, 2013, 228: S131-S136.
[23] 庞骏德, 王杨, 蔺增. 牙种植体表面喷砂酸蚀工艺的优化[J]. 中国表面工程,2014, 27(2):102-109. PANG Junde, WANG Yang, LIN Zeng. Sandblasted and acid-etched process optimization of the dental implant[J]. China Surface Engineering, 2014, 27(2):102-109.

Metrics

Viewed

Full text

Abstract

Cited

Shared

Discussed

Comments

Recommended 0

No Suggested Reading articles found!

Influence of different acid-etching time on the surface morphology and corrosion resistance of TC4 titanium alloys after sandblasting

PDF (PC)

Abstract

Cite this article

share this article

References

Related Articles 8

Metrics

Comments

Recommended 0

[1]	YAO Zhanyong, ZHANG Hao, SHANG Qingsen, GONG Benhui, LIU Zhihang, WANG Xugang. Properties of cement stabilized weathered granite material under the influence of soluble salt [J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2016, 46(2): 85-93.
[2]	ZHOU Ting-ting1, DU Ai-ling1*, GAO Yu1, YANG Yan-ling2. Influence of pH value in a phosphating bath on zinc phosphate coatings on the AZ61 magnesium alloy [J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2011, 41(1): 114-119.
[3]	HUO Wen-Guo, XU Jiu-Hua, FU Yu-Can. Study of abrasive wear in belt grinding of a close alpha titanium alloy [J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2010, 40(1): 53-58.
[4]	SUN Ji, LI Jian-feng. Study of key technologies of titanium monolithic components machining [J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2009, 39(3): 81-88.
[5]	GAO Yu, DU Ai-ling, YANG Yan-ling. Influence of zinc oxide in a phosphating bath on phosphate coating on AZ61 magnesium alloy [J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2009, 39(3): 77-80.
[6]	LIU Zhanqiang, AI Xing, LI Tiantian, WAN Yi. Machinability analysis of Ti6Al4V alloy with PCBN tools in turning operations [J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2009, 39(1): 77-83.
[7]	LIU Xue-wen,SHI Yuan-chang,BAI Qi-ya . Corrosion resistance properties in seawater of sintering Al₂O₃ ceramics [J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2008, 38(5): 113-116 .
[8]	PANG Zhi-min,TIAN Lan,HOU Zheng-xin . The improvement of the cochlear implantation CIS speech processing method based on the all phase DFT filter [J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2007, 37(1): 35-38 .