亚甲基蓝自二氧化硅@磷酸八钙载药颗粒的释放行为

李成峰,刘群,王文浩,王百威,杨赞中   

  1. 山东理工大学材料科学与工程学院, 山东 淄博 255049
  • 收稿日期:2015-12-02 出版日期:2016-06-30 发布日期:2015-12-02
  • 作者简介:李成峰(1979— ),男,山东青州人,副教授,博士,主要研究方向为生物医用材料. E-mail: cfli@sdut.edu.cn
  • 基金资助:
    山东省自然科学基金资助项目(ZR2013EML008,ZR2012EMM016);山东省高等学校科技计划资助项目(J11LD52);山东省科技发展计划资助项目(2014GZX201008)

Investigation of the release behavior of methylene blue from silica@octacalcium phosphate as drug carrier

LI Chengfeng, LIU Qun, WANG Wenhao, WANG Baiwei, YANG Zanzhong   

  1. School of Materials Science and Engineering, Shandong University of Technology, Zibo 255049, Shandong, China
  • Received:2015-12-02 Online:2016-06-30 Published:2015-12-02

摘要: 采用改性的Pechini方法在含亚甲基蓝(methylene blue, MB)的二氧化硅颗粒(silica-MB)表面沉积磷酸八钙(octacalcium phosphate, OCP)后制备得到silica-MB@OCP,研究制备工艺条件对载药颗粒的结构、药物释放行为和载体降解性能的影响规律。研究发现聚乙二醇(polyethylene glycol, PEG)的分子量、PEG和柠檬酸的添加量对载药颗粒的物相、化学组成和形貌有显著影响。MB释放量和单体/二聚体的比例随时间的变化规律都对载药颗粒的结构和溶液pH值条件敏感,这与MB分子扩散行为受OCP壳层的结构和溶液条件影响有关。相比于silica-MB, silica-MB@OCP在磷缓冲液和lysosome-like缓冲液中的降解比例要高得多,这是由于MB扩散行为对颗粒结构的破坏产生显著影响导致的。

关键词: 药物缓释, 磷酸八钙, 亚甲基蓝, 二氧化硅, 降解

Abstract: A modified Pechinni method was employed to synthesize the drug carrier of silica-MB@OCP, which was achieved through deposition of octacalcium phosphate(OCP)on MB-loaded silica particle(silica-MB). The influences of reaction conditions on structural evolution of drug carrier, modulation of release behaviors and decomposition of drug vehicle were studied. The phase, chemical constitution and morphology of silica-MB@OCP were significantly influenced by the molecular weight of polyethylene glycol(PEG), adding amount of PEG and citric acid. The variations of the cumulative release and the ratio of monomer versus dimers of MB with time were sensitivity with the structure of silica-MB@OCP and the pH value of culture solution, which influenced the diffusion of MB. In comparison with those of silica-MB, the degradation ratios of silica-MB in phosphate buffered saline and lysosome-like buffer were much higher as a result of the influence of MB diffusion on the destruction of drug carrier.

Key words: sustained-release behavior, octacalcium phosphate, degradation, silica, methylene blue

中图分类号: 

  • TQ174
[1] ZHANG S, CHU Z, YIN C, et al. Controllable drug release and simultaneously carrier decomposition of SiO2-drug composite nanoparticles[J]. Journal of the American Chemical Society, 2013, 135(15):5709-5716.
[2] 张爱娟,高增丽,王卫伟,等. 有机泡沫浸渍法制备多孔羟基磷灰石生物支架的研究[J]. 山东大学学报(工学版),2012, 42(3):105-111. ZHANG Aijuan, GAO Zengli, WANG Weiwei, et al. Study of the porous hydroxyapatite scaffold prepared by dipping with polymer foams[J]. Journal of Shandong University(Engineering Science), 2012, 42(3):105-111.
[3] LAI C Y, BRIAN G T, DUSAN M J, et al. A mesoporous silica nanosphere-based carrier system with chemically removable CdS nanoparticle caps for stimuli-responsive controlled release of neurotransmitters and drug molecules[J]. Journal of the American Chemical Society, 2003, 125(15):4451-4459.
[4] GAI S L, YANG P P, LI C X, et al. Synthesis of magnetic, up-conversion luminescent, and mesoporous core-shell-structured nanocomposites as drug carriers[J]. Advanced Functional Materials, 2010, 20(7):1-7.
[5] DU L, LIAO S, KHATIB H A, et al. Controlled-access hollow mechanized silica nanocontainers[J]. Journal of the American Chemical Society, 2009, 131(42):15136-15142.
[6] TSYALKOVSKY V, BURTOVYY R, KLEP V, et al. Fluorescent nanoparticles stabilized by poly(ethylene glycol)containing shell for pH-triggered tunable aggregation in aqueous environment[J]. Langmuir, 2010, 26(13):10684-10692.
[7] SCHLOSSBAUER A, KECHT J, BEIN T. Biotin-avidin as a protease-responsive cap system for controlled guest release from colloidal mesoporous silica[J]. Angew Chem Int Ed, 2009, 48(17):3092-3095.
[8] 李成峰,王燕云,杜健,等. 二氧化硅@羟基磷灰石颗粒的制备及其药物装载与体外释放行为研究[J]. 人工晶体学报,2015, 44(3):830-835. LI Chengfeng, WANG Yanyun, DU Jian, et al. Synthesis of core-shell structured silica@hydroxyapatite for drug storage and its release behavior in vitro[J]. Journal of Synthetic Crystals, 2015, 44(3):830-835.
[9] LI C F, GE X L, LI Y D, et al. Modulation of release behaviors of methylene blue from degradable silica-methylene blue@octacalcium phosphate powders with different shell structures[J]. Colloids Surface A, 2015, 472:78-84.
[10] TARDIVO J P, GIGLIO A D, OLIVEIRA C S, et al. Methylene blue in photodynamic therapy: from basic mechanisms to clinical applications[J]. Photodiaqnosis and Photodynamic Therapy, 2005, 2:175-191.
[11] WAINWRIGHT M. Non-porphyrin photosensitizers in biomedicine[J]. Chemical Society Review, 1996, 25:351-359.
[12] DEMBSKI S, RUPP S, GELLERMANN C, et al. Luminescent silicate core-shell nanoparticles: synthesis, functionalization, optical, and structural properties[J]. Journal of Colloid and Interface Science, 2011, 358(1):32-38.
[13] KONG HDY, YU M, LIN CK, et al. Sol-gel Synthesis and characterization of Zn2SiO4:Mn@SiO2 spherical core-shell particles[J]. Journal of Electrochemical Society, 2005, 152(9):H146-H151.
[14] DEMBSKI S, MILDE M, DYRBA M, et al. Effect of pH on the synthesis and properties of luminescent SiO2/calcium phosphate:Eu3+ core-shell nanoparticles[J]. Langmuir, 2011, 27(23):14025-14032.
[15] GE X L, LI C F, FAN C Y, et al. Enhanced photoluminescence properties of methylene blue dye encapsulated in nanosized hydroxyapatite/silica particles with core-shell structure[J]. Applied Physics A, 2013, 113(3):583-589.
[16] LI C, LI Y, BAI J, et al. Release behavior of methylene blue dimers from silica-methylene blue@octacalcium phosphate powders in phosphate buffer saline and lysosome-like buffer[J]. Journal of Sol-Gel Science and Technology, 2015, 75(2):397-406.
[17] YAO H, LI N, XU S, et al. Electrochemical study of a new methylene blue/silicon oxide nanocomposition mediator and its application for stable biosensor of hydrogen peroxide[J]. Biosensors and Bioelectronics, 2005, 21(2):372-377.
[18] YAN Y, ZHANG M, GONG K, et al. Adsorption of methylene blue dye onto carbon nanotubes: a route to an electrochemically functional nanostructure and its layer-by-layer assembled nanocomposite[J]. Chemistry of Materials, 2005, 17(13):3457-3463.
[19] CHANG S J, LIAO W S, CIOU C J, et al. An efficient approach to derive hydroxyl groups on the surface of barium titanate nanoparticles to improve its chemical modification ability[J]. Journal of Colloid and Interface Science, 2009, 329(2):300-305.
[20] MIRTH G, LERCHER J A. Coadsorptlon of toluene and methanol on HZSM-5 zeolites[J]. Journal of Physical Chemistry, 1991, 95(9):3736-3740.
[21] ROELOFS F, VOGELSBERGER W. Dissolution of commercial microscale quartz particles in water at biological-like conditions and its theoretical description[J]. Journal of Physical Chemistry C, 2013, 117(27):13914-13927.
[22] 李成峰,高天宇,贺立群,等. HAp/mSiO2载药颗粒的制备及体外药物释放行为[J]. 硅酸盐学报, 2014, 42(4):464-470. LI Chengfeng, GAO Tianyu, HE Liqun, et al. Synthesis and in vitro release behavior of core-shell structured hydroxyapatite/mesoporous silica powders with drug storage[J]. Journal of the Chinese Ceramic Society, 2014, 42(4):464-470.
[23] SHEN D, YANG J, LI X, et al. Biphase stratification approach to three-dimensional dendritic biodegradable mesoporous silica nanospheres[J]. Nano Letters, 2014, 14(2):923-932.
[24] MITCHELL K K P, LIBERMAN A, KUMMEL A C, et al. Iron(III)-doped, silica nanoshells: a biodegradable form of silica[J]. Journal of the American Chemical Society, 2012, 134(34):13997-14003.
[25] ASHLEY C E, CARNES E C, PHILLIPS G K, et al. The targeted delivery of multicomponent cargos to cancer cells via nanoporous particle-supported lipid bilayers[J]. Nature Materials, 2011, 10(5):389-397.
[1] 于正刚,常宁,赵根源,石春颖,周爱秋. Bi7Ti4NbO21的合成、酸化及光催化性能[J]. 山东大学学报(工学版), 2017, 47(2): 106-110.
[2] 时琼,梁爽,王曙光*. 零价铁联合微生物去除水中高氯酸盐的研究[J]. 山东大学学报(工学版), 2012, 42(6): 107-114.
[3] 张保良1,王洪运1,秦绪平1*,赵芳1,冯维红1,郭波2. Poly(AM/AMPS)反相乳液的Hofmann降解及其在脱除Cu2+方面的应用[J]. 山东大学学报(工学版), 2011, 41(1): 126-132.
[4] 李文静 施来顺 刘艳璞 余锋俊 董岩岩. 二氧化锰催化二氧化氯氧化处理萘酚绿模拟废水的实验研究[J]. 山东大学学报(工学版), 2008, 38(6): 76-81.
[5] 李善评,赵玉晓,乔鹏,冯正志 . 好氧颗粒污泥的培养及基质降解和污泥生长动力学分析[J]. 山东大学学报(工学版), 2008, 38(3): 95-98 .
[6] 牛秀明,傅春华 . 炭在脉冲放电过程中对污水中有机物的降解作用[J]. 山东大学学报(工学版), 2008, 38(1): 121-126 .
[7] 施来顺,董岩岩,李彦彦,李文静 . 二氧化氯催化氧化处理铬黑T模拟废水的实验[J]. 山东大学学报(工学版), 2007, 37(5): 113-117 .
[8] 姜峰,李青海,李剑峰,李方义,魏宝坤 . 基于LCA法的包装材料环境友好性的评价[J]. 山东大学学报(工学版), 2006, 36(6): 10-13 .
[9] 施来顺,朱红梅,董岩岩,李彦彦 . 二氧化氯催化氧化处理萘酚绿模拟废水的实验研究[J]. 山东大学学报(工学版), 2006, 36(4): 91-95 .
[10] 张英,郎咏梅,赵玉晓,张鉴达,乔鹏,李善评 . 由EGSB厌氧颗粒污泥培养好氧颗粒污泥的工艺探讨[J]. 山东大学学报(工学版), 2006, 36(4): 56-59 .
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
[1] 李可,刘常春,李同磊 . 一种改进的最大互信息医学图像配准算法[J]. 山东大学学报(工学版), 2006, 36(2): 107 -110 .
[2] 岳远征. 远离平衡态玻璃的弛豫[J]. 山东大学学报(工学版), 2009, 39(5): 1 -20 .
[3] 程代展,李志强. 非线性系统线性化综述(英文)[J]. 山东大学学报(工学版), 2009, 39(2): 26 -36 .
[4] 王勇, 谢玉东.

大流量管道煤气的控制技术研究

[J]. 山东大学学报(工学版), 2009, 39(2): 70 -74 .
[5] 刘新1 ,宋思利1 ,王新洪2 . 石墨配比对钨极氩弧熔敷层TiC增强相含量及分布形态的影响[J]. 山东大学学报(工学版), 2009, 39(2): 98 -100 .
[6] 田芳1,张颖欣2,张礼3,侯秀萍3,裘南畹3. 新型金属氧化物薄膜气敏元件基材料的开发[J]. 山东大学学报(工学版), 2009, 39(2): 104 -107 .
[7] 陈华鑫, 陈拴发, 王秉纲. 基质沥青老化行为与老化机理[J]. 山东大学学报(工学版), 2009, 39(2): 125 -130 .
[8] 赵延风1,2, 王正中1,2 ,芦琴1,祝晗英3 . 梯形明渠水跃共轭水深的直接计算方法[J]. 山东大学学报(工学版), 2009, 39(2): 131 -136 .
[9] 李士进,王声特,黄乐平. 基于正反向异质性的遥感图像变化检测[J]. 山东大学学报(工学版), 2018, 48(3): 1 -9 .
[10] 赵科军 王新军 刘洋 仇一泓. 基于结构化覆盖网的连续 top-k 联接查询算法[J]. 山东大学学报(工学版), 2009, 39(5): 32 -37 .