GE Zhi1, MENG Fanbo2, YUE Hongya1, HU Yizhang1   

  1. 1.School of Civil Engineering, Shandong University, Jinan 250061, Shandong, China;
    2.Shandong Experimental High School, Jinan 250000, Shandong, China
  • Received:2014-02-21 Online:2014-04-20 Published:2014-02-21

Abstract: PET was used as binder to produce PET-brick powder mortar. The water absorption, sulfate resistance, and chloride penetration resistance of the mortar were investigated. The SEM test was performed to exam the microstructure. The test results showed that the absorption was 0.9% after  7 days. After 20 cycles, the difference in compressive strength was only 1.83% for samples in the sulfate solution and water. The sample had low chloride permeability with a test result of 48 C. The  test results showed that  the PET-brick powder mortar had high durability. The SEM results indicated that the mortar had uniform structure with very small amount of pores inside.

Key words: PET-brick powder mortar, water absorption rate, chloride permeability, sulfate resistance

CLC Number: 

  • TU528.41
No related articles found!
Viewed
Full text
221
HTML PDF
Just accepted Online first Issue Just accepted Online first Issue
0 0 0 221 0 0

  From Others local
  Times 25 196
  Rate 11% 89%

Abstract
999
Just accepted Online first Issue
999 0 0
  From Others
  Times 999
  Rate 100%

Cited

Web of Science  Crossref   ScienceDirect  Search for Citations in Google Scholar >>
 
This page requires you have already subscribed to WoS.
  Shared   
  Discussed   
No Suggested Reading articles found!