甲基丙烯酸十八酯基油溶性聚合物反应过程的在线红外研究

山东大学学报(工学版) ›› 2011, Vol. 41 ›› Issue (2): 144-148.

甲基丙烯酸十八酯基油溶性聚合物反应过程的在线红外研究

韩涛1, 王晓云2,于萍1*, 代晓东3,吕小博1,李冰1

1. 山东大学化学与化工学院, 山东济南 250061; 2. 山东省化工研究院, 山东济南 250014;
3.中石油管道公司管道研究中心, 河北廊坊 065000

收稿日期:2010-09-02 出版日期:2011-04-16 发布日期:2010-09-02
通讯作者: 于萍(1963- ),女,山东威海人,副教授,主要研究方向为化学工程.Email:yupping@sdu.edu.cn E-mail:yupping@sdu.edu.cn
作者简介:韩涛(1983- ),男,山东青岛人,硕士研究生,主要研究方向为高分子石油化工.Email:hantao-307@163.com
基金资助:
国家重点基础研究发展计划资助项目(2008CB617508)

React IR^TM study of the synthesis of octadecyl methacrylate-based
oil soluble polymer

HAN Tao1, WANG Xiaoyun2, YU Ping1*, DAI Xiaodong2, L Xiaobo1, LI Bing1

1. School of Chemistry and Chemical Engineering, Jinan 250061, China;
2. Chemical Technology Academy of Shandong Province, Jinan 250014, China;
3 China National Petroleum Pipeline Corporation Pipeline Research Center, Langfang 065000, China

Received:2010-09-02 Online:2011-04-16 Published:2010-09-02

摘要/Abstract

摘要：

采用React IRTM 4000在线红外检测装置和AutoRC(reaction calorinleter)等温反应量热器对以甲基丙烯酸十八酯、马来酸酐、苯乙烯为原料的三元共聚过程进行了反应动力学研究和热量变化研究。研究结果表明,酯基、酸酐、苯环的吸光度随时间变化基本保持不变;C=C键断裂过程中吸光度随时间的变化情况对应了三元加成共聚反应控制区;引发剂发挥引发作用需要一定的诱导期;加成聚合反应有较明显放热区,但是整个反应仍可视为相对平稳、反应温和,从而为合成工艺关键控制参数的确定和优化提供了依据。

关键词: 甲基丙烯酸十八酯-马来酸酐-苯乙烯三元共聚物, 在线红外检测装置；等温反应量热

Abstract:

The kinetics of the copolymerizing process of octadecyl methacrylate, styrene and maleic anhydride were performed by using the react IR analytical system (React IR^TM4000), and the heat flow derived from exothermic copolymerization was measured by an Auto-RC reaction calorimeter. The results showed that the absorbance of functional groups, i.e. ester, anhydride, and phenyl remained stable. The change of the absorbance with time corresponded to the ternary addition copolymerization control region when the CC bond was broken. The initiator required a certain inductiona period. There was an apparent exothermic reaction zone in the additional polymerization, while reaction was relatively stable and moderate. Therefore, this study could provide the reference for the determination and optimization of key control parameters of the synthesis process.

Key words: octadecyl methacrylate-styrene-maleic anhydride terpolymer, the react IR system, reaction calorimeter

韩涛1, 王晓云2,于萍1*, 代晓东3,吕小博1,李冰1. 甲基丙烯酸十八酯基油溶性聚合物反应过程的在线红外研究[J]. 山东大学学报(工学版), 2011, 41(2): 144-148.

HAN Tao1, WANG Xiaoyun2, YU Ping1*, DAI Xiaodong2, L Xiaobo1, LI Bing1. React IR^TM study of the synthesis of octadecyl methacrylate-based
oil soluble polymer[J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2011, 41(2): 144-148.

参考文献

多维度评价

Viewed

Full text

Abstract

Cited

Shared

Discussed

本文评价

推荐阅读 10

[1]	李侃 . 嵌入式相贯线焊接控制系统开发与实现[J]. 山东大学学报(工学版), 2008, 38(4): 37 -41 .
[2]	来翔 . 用胞映射方法讨论一类MKdV方程[J]. 山东大学学报(工学版), 2006, 36(1): 87 -92 .
[3]	余嘉元1 , 田金亭1 , 朱强忠2 . 计算智能在心理学中的应用[J]. 山东大学学报(工学版), 2009, 39(1): 1 -5 .
[4]	陈瑞,李红伟,田靖. 磁极数对径向磁轴承承载力的影响[J]. 山东大学学报(工学版), 2018, 48(2): 81 -85 .
[5]	王波,王宁生 . 机电装配体拆卸序列的自动生成及组合优化[J]. 山东大学学报(工学版), 2006, 36(2): 52 -57 .
[6]	张英,郎咏梅,赵玉晓,张鉴达,乔鹏,李善评 . 由EGSB厌氧颗粒污泥培养好氧颗粒污泥的工艺探讨[J]. 山东大学学报(工学版), 2006, 36(4): 56 -59 .
[7]	王丽君,黄奇成,王兆旭 . 敏感性问题中的均方误差与模型比较[J]. 山东大学学报(工学版), 2006, 36(6): 51 -56 .
[8]	Yue Khing Toh1 ， XIAO Wendong2 ， XIE Lihua1 . 基于无线传感器网络的分散目标跟踪：实际测试平台的开发应用（英文）[J]. 山东大学学报(工学版), 2009, 39(1): 50 -56 .
[9]	孙炜伟,王玉振. 考虑饱和的发电机单机无穷大系统有限增益镇定[J]. 山东大学学报(工学版), 2009, 39(1): 69 -76 .
[10]	孙玉利,李法德,左敦稳,戚美 . 直立分室式流体连续通电加热系统的升温特性[J]. 山东大学学报(工学版), 2006, 36(6): 19 -23 .