JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE) ›› 2015, Vol. 45 ›› Issue (1): 82-87.doi: 10.6040/j.issn.1672-3961.0.2014.196

Previous Articles     Next Articles

Effects of reaction conditions on the size distribution of iron phosphate

LUO Yanhua1,2, SHE Shijie2, CAO Weiguo1, PAN Feng1,3   

  1. 1. School of Chemical Engineering, Nanjing University of Science and Technology, Nanjing 210094, Jiangsu, China;
    2. Anhui Tianyuan Technology Co. Ltd, Sinosteel Corporation, Maanshan 243000, Anhui, China;
    3. National Quality Supervision and Inspection Center for Industrial Explosive Materials, Nanjing 210094, Jiangsu, China
  • Received:2014-07-17 Revised:2015-01-08 Published:2014-07-17

Abstract: The process parameters of preparing iron phosphate in ethanol system were optimized by the method of orthogonal experiment. The results showed that the influencing order of the parameters affecting the particle size distribution of iron phosphate was ethanol addition rate, reaction temperature and stirring speed. The ethanol adding speed was the key factor to influence the size distribution of iron phosphate. When the addition of ethanol was 40 L/min, the reaction temperature was 90 ℃ and the stirring speed was 60 r/min, the d50 of iron phosphate was 0.73 μm. When the addition of ethanol was 10 L/min, the reaction temperature was 50 ℃ and the stirring speed was 120 r/min, the d50 of iron phosphate was 2.10 μm. The physical-chemical indicators of iron phosphate were charaterized by SEM, BET and XRF. When d50 was 0.73 μm, the BET of iron phosphate was larger than 60 m2/g. When d50 was 2.10 μm, the BET of iron phosphate was approximately 45 m2/g. The molar ratio of P and Fe of two kinds of iron phosphate was about 1:1. The content of sulfur was relatively high, when the particle size of iron phosphate was smaller.

Key words: ethanol, iron phosphate, orthogonal experiment, particle size, sulfur content

CLC Number: 

  • O614.81
[1] LI Meijun, WU Zili, MA Zhen, et al. CO oxidation on Au/FePO4 catalyst: reaction pathways and nature of Au sites[J]. Journal of Catalysis, 2009, 266:98-105.
[2] MC CORMICK R L, ALPTEKIN G O. Comparison of alumina-, silica-, titania-, and zirconia—supported FePO4 catalysts for selective methane oxidation[J]. Catalysis Today, 2000, 55:269-280.
[3] ALDON L, PEREA A, WOMES M, et al. Determination of the Lamb-Mssbauer factors of LiFePO4 and FePO4 for electrochemical in situ and operando measurements in Li-ion batteries[J]. Journal of Solid State Chemistry, 2010, 183:218-222.
[4] LI Gang, YANG Zhanxu, YANG Wensheng. Effect of FePO4 coating on electro-chemical and safety performance of LiCoO2 as cathode material for Li-ion batteries[J]. Journal of Power Sources, 2008, 183:741-748.
[5] 迪丽拜尔·阿合买提,艾尔肯·吐尔逊,肖开提·阿布力孜,等. 磷酸铁纳米薄膜符合光波导氨气传感原件的制备[J]. 应用化学,2010, 27(8):965-969. Dilbar Ahmat, Erkin Tursun, Xawkat Abliz, et al. Fabrication of composite optical wave-guides based onthin films consisted of iron phosphate nanoparticles and their applications as ammonia gas sensor[J]. Chinese Journal of Applied Chemistry, 2010, 27(8):965-969.
[6] 郭学锋. 纳米及介孔材料的制备、表征和催化性能研究[D]. 南京: 南京大学, 2000. GUO Xuefeng. Researched on preparation, characterization and catalytic properties of nano-crystalline and mesoporous materials[D]. Nanjing: Nanjing University, 2000.
[7] WANG Ye, Kiyoshi Otsuka. Partial oxidation of ethane by reductively activated oxygen over iron phosphate catalyst[J]. Journal of Catalysis, 1997, 171(1):106-114.
[8] 叶焕英,郑曲模,陈骏驰,等. 超细二水磷酸铁的制备研究[J]. 无机盐工业,2012, 44(4):59-61. YE huanying, ZHENG Qumo, CHEN Junchi, et al. Preparation of ultrafine iron phosphate dihydrate[J]. Inorganic Chemicals Industry, 2012, 44(4):59-61.
[9] ZHANG S M, ZHANG J X, XU S J, et al. Li ion diffusivity and electrochemical properties of FePO4 nanoparticles acted directly as cathode materials in lithium ion rechargeable batteries[J]. Electrochimica Acta, 2013, 88:287-293.
[10] SHI Z C, ATTIA A, YE W L, et al. Synthesis, characterization and electrochemical performance of mesoporous FePO4 as cathode material for rechargeable lithium batteries[J]. Electrochemical Solid-Stated Letter, 2008, 53:2665-2673.
[11] MASQUELIER P, REALE C, WURM M, et al. Hydrated iron phosphates FePO4·nH2O and Fe4(P2O7)3·nH2O as 3V positive electrodes in rechargeable lithium batteries[J]. Journal of the Electrochemical Society, 2002, 149(8):A1037-A1044.
[12] DONGYEON SON, KIM EUNJIN, KIM TAEGON, et al. Nanoparticle iron phosphate anode material for Li-ion battery[J]. Application Physicis Letter, 2004, 85(24):5875-5879.
[13] ZAGHIB K, JULIEN C M. Structure and electrochemistry of FePO4·2H2O hydrate[J]. Journal of Power Sources, 2005, 142(1):279-284.
[14] 罗西佳,肖仁贵,曹建新,等. 介质对磷酸铁结晶影响的研究[J]. 贵州大学学报:自然科学版, 2011, 28(6):48-51. LUO Xijia, XIAO Rengui, CAO Jianxin, et al. Study of iron(Ⅲ) phosphate obtained from different media[J]. Journal of Guizhou University:Natural Sciences, 2011, 28(6):48-51.
[15] 周玉琳. 由钛白废副硫酸亚铁制备锂离子电池正极材料磷酸铁锂用前驱体磷酸铁的工艺研究[D]. 长沙: 中南大学, 2008. ZHOU Yulin. Study of iron(Ⅲ) phosphate prepared LiFePO4 from ferrous sulfate of TiO2 waste vice[D]. Changsha: Zhongnan University, 2008.
[16] 张震,蒲薇华,任建国,等. 控制结晶法制备球形磷酸铁的团聚尺寸模型[J]. 化学工程,2011, 39(8):20-24. ZHANG Zhen, PU Weihua, REN Jianguo, et al. Agglomeration-size model of ferric phosphate spherical particle prepared by controlled crystallization [J]. Chemical Engineering, 2011, 39(8):20-24.
[17] 吴云胜. 低热固相反应法制备水合磷酸铁正极材料即其充放电性能研究[D]. 南京: 南京师范大学, 2011. WU Yunsheng. Prepared hydrated iron phosphate under low temperature solid state reaction and researched on the charge and discharge properties of cathode materials [D]. Nanjing: Nanjing Normal University, 2011.
[18] GUO Xuefeng, DING Weiping, CHEN Hong, et al. Preparation and characterization of nanosized Fe-P-O catalyst[J]. Journal of Fuel Chemical and Technology, 2000, 28(5):385-390.
[19] ROHNER F, EMST F O, ARNOLD M, et al. Synthesis characterization and bioavailability in rats of fettic phosphate nanoparticles[J]. Nutrition Research Reviews, 2007, 137:614-618.
[20] GABERSCEK M, DOMIKO R, JAMNIK, J. Is small particle size more important than carbon coating an example study on LiFePO4 cathodes?[J]. Electrochemical Communication, 2007, 9:2778-2783.
[21] HUANG Y H, REN H B, YIN S Y, et al. Synthesis of LiFePO4/C composite with high-rate performance by starch sol assisted rheological phase method[J]. Journal of Power Sources, 2010, 195(2):610-613.
[22] ZHANG Tongbao, LU Yangcheng, LUO Guangsheng. Size adjustment of iron phosphate nanoparticles by using mixed acids[J]. Industrial & Engineering Chemistry Research, 2013(52):6962-6968.
[23] 刘学蔚,侯绪浩,陈怡憓,等. 正交优化白及多糖复合支架材料的实验研究[J]. 山东大学学报:医学版,2014, 52(3):1-5. LIU Xuewei, HOU Xuhao, CHEN Yihui, et al. Experimental study of the bletilla glucomanna composited scaffolds by orthogonal experiment[J]. Journal of Shandong University: Health Sciences, 2014, 52(3):1-5.
[24] JEFF WU C F, MICHAEL Hamada.实验设计与分析及参数优化[M]. 张润楚,郑海涛,兰燕,等,译. 北京:中国统计出版社, 2002:176-225. JEFF WU C F, MICHAEL Hamada. Design and analysis of experiments and parameter optimization[M]. ZHANG Runchu, ZHENG Haitao, LAN Yan, et al, trans. Beijing: China Statistical Publishing House, 2002:176-225.
[25] NIELSEN A E. Kinetics of precipitation [M]. Oxford: Pergamon Press, 1964:350-355.
[26] DIRKSEN J A, RING T A. Fundamentals of crystallization: kinetic effects on particle size distributions and morphology[J]. Chemical Engineering Sciences, 1991, 46(10):2389-2427.
[1] DONG Zhen, YANG Yonglu, XIONG Guodong, LAI Yanhua, LYU Mingxin. Preparation and optimization of compound bonded material used in reducing the contact thermal resistance [J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2017, 47(3): 143-150.
[2] ZHANG Luchen, LI Shuchen, LI Shucai, LIAO Qikai. Effect on the performance of shotcrete mixed with silica fume and fly ash [J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2016, 46(5): 102-109.
[3] SHI Jing. Effect of organic alkali ethanolamine on the interfacial tensions of Shengli crude oils [J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2013, 43(3): 70-74.
[4] YANG Jin-bei1, 3, YU Mei-qiong1, ZHENG Zhi-gong2, QIU Ting3*. Simulation for separation of ethyl acetate and ethanol by heat-integrated pressure swing distillation [J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2013, 43(1): 109-114.
[5] CUI Nai-xin, ZHAO Fang-fang, LIANG Bing, GAI Di. Experiment on internal particle size distribution law of a waste dump [J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2012, 42(2): 52-57.
[6] GE Zhi1, WANG Hao2*, ZHENG Li1, MAO Hong-lu1. Properties of concrete containing recycled clay brick powde [J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2012, 42(1): 104-105.
[7] WANG Gang1, 2, JIANG Yu-jing2, LI Shucai3. Rapid feedback analysis method for underground caverns during constructing [J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2011, 41(4): 133-136.
[8] ZHANG Ke-Song, HU Jing-Na, LIU Yun-Gang, BAO Xiao-Feng. Investigation of three-way catalyst performanceusing ethanol-gasoline and normal gasoline [J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2010, 40(1): 149-153.
[9] YANG Jing,YUE Qin-yan,LI Ying,LI Ren-bo,GAO Bao-yu . Application of modified activated carbon fiber in the treatment of phosphorus-containing wastewater [J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2008, 38(1): 92-95 .
[10] SHEN Xiang,LI Musen,CAO Ning,WANG Chengxiang,L Yupeng,BAI Yunqiang . The dispersant effect on HA powder prepared by chemical [J]. JOURNAL OF SHANDONG UNIVERSITY (ENGINEERING SCIENCE), 2006, 36(3): 5-08 .
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
No Suggested Reading articles found!